ER308 符合：YB/T5092 H08Cr21Ni10Si
不锈钢焊丝 相当：AWS A5.9 ER308
ISO 14343-B-SS308
In accordance with：YB/T5092 H08Cr21Ni10Si
Be equivalent to：AWS A5.9 ER308
ISO 14343-B-SS308
说明：ER308焊丝主要成分是18Cr-8Ni。配用SJ601不锈钢碱性烧结焊剂，其焊缝金属具有良好的力学性能和抗晶间腐蚀性能，焊缝抗裂性良好；具有不增Si、不增C，且Cr、Ni烧损小等特点。
用途：广泛应用于石油化工等行业，如12Cr18Ni9（SUS302）、06Cr19Ni10（SUS304）等材料的焊接。
Instructions：The ER308 welding stick consists mainly of 18Cr-8Ni. It coordinates with the stainless steel alkaline sintered flux SJ601. It’s welding line metal has good mechanical properties and resistance ability to intergranular corrosion and crack. It would not increase Si or C and would burn little Cr and Ni.
Use: It’s widely used to weld materials in many industries like petrochemical industry, such as 12Cr18Ni9（SUS302）and 06Cr19Ni10（SUS304）.
焊丝化学成分（%）
|
项目
|
C
|
Mn
|
Si
|
Cr
|
Ni
|
Mo
|
P
|
S
|
Cu
|
|
保证值
|
≤0.08
|
1.00～2.50
|
0.30～0.65
|
19.50～22.00
|
9.00～11.00
|
≤0.75
|
≤0.030
|
≤0.030
|
≤0.75
|
|
例值
|
0.040
|
1.80
|
0.31
|
20.15
|
9.52
|
0.43
|
0.013
|
0.008
|
0.34
|
参考电流（DC+）
|
焊丝直径（mm）
|
Φ0.8
|
Φ1.0
|
Φ1.2
|
Φ1.6
|
Φ2.0
|
Φ2.5
|
Φ3.2
|
|
焊接电流（A）
|
70～150
|
100～200
|
140～220
|
50～100
|
100～200
|
200～300
|
300～400
|
注意事项：
1. 保护气体：注意保护气体的纯度，混合气配比推荐Ar+1～3%O2。TIG采用纯Ar。
2. 气体流量：20～25L/min。
3. 干伸长度：15～25mm。
4. 将焊接部位的锈层、湿气、油污、灰尘等确实除净。
5. 室外焊接时，当风速大于1.5m/s应采取适当的防风措施，以防发生气孔。
以上建议仅供参考，在具体操作中以现场情况为准。必要时先进行工艺评定再确定焊接方案。