ER310 符合：YB/T5092 H12Cr26Ni21Si
不锈钢焊丝 相当：AWS A5.9 ER310
ISO 14343-A-G 25 20
In accordance with：YB/T5092 H12Cr26Ni21Si
Be equivalent to：AWS A5.9 ER310
ISO 14343-A-G 25 20
说明：焊丝主要成分是25Cr-20Ni，是不锈钢MIG、TIG焊接材料，可全位置焊接。耐高温性能稳定，可达1200℃。焊接作业性极佳—送丝顺畅、电弧稳定、成形美观、飞溅极少；熔敷金属的机械性能稳定。
用途：常用于耐高温产品如高温炉、煤炭焦化设备等，也可应用于复合层堆焊和异种钢的焊接。
Instructions：The ER310 welding stick consists mainly of 25Cr-20Ni. It belongs to stainless steel MIG and TIG welding material and can be used to all-position welding. It has stable performance to resist high temperature up to 1200℃. It performs well while welding, with smooth wire feed, stable voltaic arc, beautiful formation and little splatter. The deposited metal has steady mechanical property.
Use：It’s usually used to weld heat resistance products, such as high temperature furnace and coal coke equipment. It can also be used to weld composite layer and dissimilar steel.
焊丝化学成分（%）
|
项目
|
C
|
Mn
|
Si
|
Cr
|
Ni
|
Mo
|
P
|
S
|
Cu
|
|
保证值
|
0.08～0.15
|
1.00～2.50
|
0.30～0.65
|
25.00～28.00
|
20.00～22.50
|
≤0.75
|
≤0.030
|
≤0.030
|
≤0.75
|
|
例值
|
0.087
|
2.00
|
0.38
|
27.42
|
21.82
|
0.35
|
0.011
|
0.009
|
0.35
|
参考电流（DC+）
|
焊丝直径（mm）
|
Φ0.8
|
Φ1.0
|
Φ1.2
|
Φ1.6
|
Φ2.0
|
Φ2.5
|
Φ3.2
|
|
焊接电流（A）
|
70～150
|
100～200
|
140～220
|
50～100
|
100～200
|
200～300
|
300～400
|
注意事项：
1. 保护气体：注意保护气体的纯度，混合气配比推荐Ar+1～3%O2。TIG采用纯Ar。
2. 气体流量：20～25L/min。
3. 干伸长度：15～25mm。
4. 将焊接部位的锈层、湿气、油污、灰尘等确实除净。
5. 室外焊接时，当风速大于1.5m/s应采取适当的防风措施，以防发生气孔。
6. 以上建议仅供参考，在具体操作中以现场情况为准。必要时先进行工艺评定再确定焊接方案。