| 材料名称：高速工具钢棒 | | | | | | | | | | | | | | | | 牌号：W6Mo5Cr4V2 | | | | | | | | | | | | | | | | 标准：GB/T 9943-1988 | | | | | | | | | | | | | | | | ●特性及适用范围： | | | | | | | | | | | | | | | | 为钨钼系通用型高速钢的代表钢号，韧性、耐磨性优于 W18Cr4V，硬度、红硬性及高温硬度相当。可用于制造各种承受冲击力较大的刀具、一般刀具大型及热塑成形刀具，也可作高负荷下的磨损的零件、冷作模具等。 | | | ●化学成份： | | | | | | | | | | | | | | | | 碳 C ：0.80～0.90(允许偏差:?0.01) | | | | | | | | | | | | | | | | 硅 Si：0.20～0.45(允许偏差:?0.05) | | | | | | | | | | | | | | | | 锰 Mn：0.15～0.40(允许偏差: 0.04) | | | | | | | | | | | | | | | | 硫 S ：≤0.030 | | | | | | | | | | | | | | | | 磷 P ：≤0.030 | | | | | | | | | | | | | | | | 铬 Cr：3.80～4.40(允许偏差:?0.05) | | | | | | | | | | | | | | | | 镍 Ni：允许残余含量≤0.30 | | | | | | | | | | | | | | | | 铜 Cu：允许残余含量≤0.25 | | | | | | | | | | | | | | | | 钒 V ：1.75～2.20(允许偏差:?0.05) | | | | | | | | | | | | | | | | 钼 Mo：4.50～5.50(允许偏差:尺寸≤6,?0.05;尺寸＞6,?0.10) | | | | | | | | | | | | | | | | 钨 W ：5.50～6.75(允许偏差:尺寸≤10,?0.10;尺寸＞10,?0.20) | | | | | | | | | | | | | | | | 注：根据供需双方协议,V的含量可为1.60～2.20 | | | | | | | | | | | | | | | | ●力学性能： | | | | | | | | | | | | | | | | 硬度 ：交货硬度:(其他加工方法)≤262HB; (退火)≤255HB。试样热处理制度及淬回火硬度:≥63HRC(箱式炉)、≥64HRC(盐浴炉) | | | | | | | | | | | | ●热处理规范及金相组织： | | | | | | | | | | | | | | | | 热处理规范：淬火,730～840℃预热，1210～1230℃(盐浴炉)或1210～1230℃(箱式炉)加热，油冷，540～560℃回火2次，每次2h。 | | | | | | | | | | | ●交货状态：热轧、锻制、冷拉钢棒以退火状态交货，热轧、锻制钢棒以退火＋其他加工方法（剥皮、轻拉、磨光或抛光等）加工后交货。 | | | | | | | | | |
|
重庆企业是一家全国知名销售世界著名品牌的模具钢企业。专业向国内模具制造企业推荐和供应质量优异的冷作工具钢、高速工具钢、热作压铸工具钢和塑胶模具钢。世界著名钢厂的卓越钢材品质和荆萌企业低价的销售策略，为公司形成庞大的用户群体，遍及台资、日资、港资、国营和私营企业。与日本日立金属“日立H1TACH1”特殊钢日本大同钢材“大同DA1DO”特殊钢瑞典UDDEHOLM“一胜百ASSAB”工具钢德国“撒斯特”特殊钢奥地利“百禄BOHLER”工具钢美国“芬可乐FKL”特殊钢及“ALCOA”铝业日本高周波“KOSHUHI”特殊钢布德鲁斯蒂森克虏伯特殊钢厂意大利鲁奇尼特殊钢厂我们将不断汇聚世界最优秀模具钢厂家之拳头产品